Bismuth antimonides, Bismuth-antimonys, or Bismuth-antimony alloys, are binary alloys of bismuth and antimony in various ratios. Some, in particular Bi0.9Sb0.1, were the first experimentally-observed three-dimensional topological insulators, materials that have conducting surface states but have an insulating interior. Various BiSb alloys also superconduct at low temperatures, are semiconductors, and are used in thermoelectric devices. Bismuth antimonide itself is sometimes described as Bi2Sb2.
Synthesis
Crystals of bismuth antimonides are synthesized by melting bismuth and antimony together under inert gas or vacuum. Zone melting is used to decrease the concentration of impurities. When synthesizing single crystals of bismuth antimonides, it is important that impurities are removed from the samples, as oxidation occurring at the impurities leads to polycrystalline growth.
Properties
Topological Insulator
Pure bismuth is a semimetal, containing a small band gap, which leads to it having a relatively high conductivity. When the bismuth is doped with antimony, the conduction band decreases in energy and the valence band increases in energy. At an Sb concentration of 4%, the two bands intersect, forming a Dirac point. Further increases in the concentration of antimony result in a band inversion, in which the energy of the valence band becomes greater than that of the conduction band at specific momenta. Between Sb concentrations of 7 and 22%, the bands no longer intersect, and the Bi1−xSbx becomes an inverted-band insulator. It is at these higher concentrations of Sb that the band gap in the surface states vanishes, and the material thus conducts at its surface.
Superconductor
The highest temperatures at which Bi.4Sb.6thin film of thicknesses 150-1350A superconduct, the critical temperature Tc, is approximately 2K. Single crystal Bi.935Sb.065 can superconduct at slightly higher temperatures, and at 4.2K, its critical magnetic field Bc of 1.6T at 4.2K.
Semiconductor
is one important parameter describing semiconductors because it describes the rate at which electrons can travel through the semiconductor. At 40K, electron mobility ranged from 0.49*106 cm2/Vs at an Sb concentration of 0 to.24*106 cm2/Vs at a Sb concentration of 7.2%. This is much greater than the electron mobility of other common semiconductors like Si, which is 1400 cm2/Vs at room temperature. Another important parameter of Bi1−xSbx is the effective electron mass, a measure of the ratio of the acceleration of an electron to the force applied to an electron. The effective electron mass is.002me for x=.11 and.0009me at x=.06. This is much less than the electron effective mass in many common semiconductors. A low EEM is good for Thermophotovoltaic applications.
Thermoelectric
Bismuth antimonides are used as the n-type legs in many thermoelectric devices below room temperature. The thermoelectric efficiency, given by its figure of merit zT = σS2T/λ, where S is the Seebeck coefficient, λ is the thermal conductivity, and σ is the electrical conductivity, describes the ratio of the energy provided by the thermoelectric to the heat absorbed by the device. At 80K, the figure of merit for Bi1−xSbx peaks at 6.5*10−3/K when x = 15%. Also, The Seebeck coefficient at 80K of Bi.9Sb.1 is -140μV/K, much smaller than the Seebeck coefficient of pure bismuth, -50μV/K.