Carlosruizite and fuenzalidate are members of a solid solution series K64Na6Mg101212·12H2O, for which the end-members have X = Se for the former and X = S for the latter. With the exception of selenium, the components of these minerals are widespread constituents of the Chilean nitrate ores. Se was not known to occur in these ores until it was discovered as a major component in carlosruizite by X-ray spectroscopy in the scanning electron microscope. Subsequent analyses of several specimens of nitrate ore from scattered localities in the Chilean nitrate fields showed them all to contain Se in amounts ranging from a few parts per million to nearly 50 ppm.
Geologic occurrence
Small amounts of carlosruizite were first found in nitrate ore from two localities in the Chilean nitrate fields. Carlosruizite was found as ~200 μm platy crystals in samples of iquiqueite, Na4K3MgB24O39·12H2O, obtained by leachingcaliche amarillo from samples in the Iquique office of the former Servicio de Minas del Estado of Chile, now the National Geology and Mining Service. The field locality of these samples is not precisely known but probably lies in the vicinity of Zapiga, where caliche amarillo is especially abundant. Of the 25 species of saline minerals that have been identified in the Chilean nitrate ores, 11 are known to be associated with carlosruizite. The dense caliche amarillo containing carlosruizite consists chiefly of a fine-grained mixture of nitratine, halite, and darapskite. The residues of leaching this material in cold water contain dietzeitebriiggenire , tarapacaite, lopezite, ulexite , probertite , and gypsum.
Atomic structure
Carlosruizite is a trigonal mineral with lattice spacing a=9.59, c=27.56 Å, Z=1 and V=2,195.11. It has a structure bearing a distant resemblance to those of the alunite group. These structures are rhombohedral or trigonal, with axial lengths of about 7 Å, and contain layers consisting of sheets of tetrahedral sulfate anions joined to an Al sheet, including OH groups, and the layers are separated by K ions. Carlosruizite was, along with fuenzalidaite, the first minerals of this type in which a layer of IO3 groups occurred.
Physical properties
Carlosruizite occurs as thin, colorless to pale yellow, transparent, euhedral, platy crystals with hexagonal outline, generally <200 μm in diameter and 20 μm thick. The crystals have a pseudorhombohedral habit, flattened on with beveled edges. They are slowly soluble in H2O. Surfaces of some crystals show abundant round or elongate cavities, which probably were formerly filled with saline fluids. The crystals are brittle and break easily into multiple fragments. Hardness is on the order of 2-3. The luster is vitreous.