Fiber cementsiding is a building material used to cover the exterior of a building in both commercial and domestic applications. Fiber cement is a composite material made of cement reinforced with cellulose fibers. Originally, asbestos was used as the reinforcing material but, due to safety concerns, that was replaced by cellulose in the 1980s. Fiber cement board may come pre-painted or pre-stained or can be done so after its installation. Fiber cement siding has several benefits since it is resistant to termites, does not rot, is impact resistant, and has fireproof properties.
Usage
In appearance fiber cement siding most often consists of overlapping horizontal boards, imitating wooden siding, clapboard and imitation shingles. Fiber cement siding is also manufactured in a sheet form and is used as cladding, it's also commonly used as a soffit / eave lining and as a tile underlays on decks and in bathrooms. Fiber cement siding can also be utilized as a substitute for timber fascias and bargeboards in high fire areas.
Specifications
Sheet sizes vary slightly from manufacturer to manufacturer but generally they range between 2400 – 3000 mm in length and 900 –1200mm in width. This manufactured size minimizes on-site wastage as residential floor, wall and roof structures lay structural members at 450 or 600mm centres. When used as siding boards, widths between 130mm and 300mm are available. Fiber cement thicknesses vary between 4.5-18mm and also vary in density – the lower density resulting in a fibrous rough edge when cut and the higher density having a cleaner smoother edge when cut. Thermal resistance and sound transmission can vary greatly between fiber cement products. Fiber cement sheet products rate poorly in thermal resistance and sound transmission and separate wall insulation is highly recommended. Generally the thicker and denser the product the better resistance it will have to temperature and sound transmission.
Installation
Fiber cement cladding is a very heavy product and requires two people to carry the uncut sheets. Thin fiber cement cladding is fragile before installation and must be handled carefully because it is prone to chipping and breakage if improperly handled. Once the product is cut it may again require two people to install – one to hold the sheet flush against studwork and the other to nail the product in place. Cutting fiber cement sheeting: Sheeting can be cut to size in three ways.
Thinner sheets can be scored with a heavy duty cutting blade and snapped
Using a hand- or electric-powered "fibro cutter"
A mechanical saw using a diamond blade is needed to cut thicker and denser sheets
When hanging fiber cement sheets, an approximately gap is required between end-joints, later to be filled with caulking made for fiber cement siding. Metal step flashing is required behind overlapping seams to prevent sheathing damage from water. Hot-dipped galvanized roofing nails are used to secure the sheets. Some caution must be exercised to properly ventilate areas where fiber cement siding is being cut; long-term exposure to the silica dust generated during the installation process can cause silicosis. Fiber cement cladding can be painted or stained before or after installation. For areas of exposure, weatherproof paint must be used. Once the product is fixed the joints are usually covered with timber battens and the entire wall surface is painted.
History
Early fiber cement panels used asbestos fibers to add strength. Ludwig Hatschek patented asbestos-reinforced fiber cement in Austria in 1901 and named it "Eternit", based on the Latin term "aeternitas", meaning everlasting. In 1903, Schweizerische Eternit-Werke AG began fabricating the material in the city of Niederurnen in Switzerland. Cellulose-reinforced fiber cement products were introduced 1980s as a safe replacement for the very widely used asbestos cement products manufactured before that time.
Durability
The external cladding products require very little maintenance once installed and painted. The thicker/denser fiber cement products have excellent impact resistance but the thinner less dense products need to be protected from impact. Compared to wooden siding, fiber cement is not susceptible to termites or rot. Fiber cement siding using baseboard materials that have been classified, by accredited laboratories, as Category A according to BS EN 12467: 2004 Fiber-cement flat sheets - Product specification and test methods are sidings which are intended for applications where they may be subject to heat, high moisture and severe frost.
Fire resistance
Fiber cement cladding is a non-combustible material which is widely used in high bushfire prone areas throughout Australia. While the best possible reaction to Fire Classifications are A1 and A1Fl respectively, both of which mean "non-combustible" according to European standard EN 13501-1: 2007, as classified by a notified laboratory in Europe, some fiber cement boards only come with Fire Classification of A2 or even lower classifications, if they are tested at all.
Safety
As mentioned previously, long-term exposure to silica dust generated by cutting fiber cement siding during installation can lead to silicosis and other lung diseases among workers. Researchers at the US National Institute for Occupational Safety and Health confirmed these findings, showing that many of the silica dust particles are in the respirable fraction, able to penetrate the deepest parts of the lung. Laboratory tests performed by cutting fiber cement siding within an isolated chamber showed that by connecting a regular shop vacuum to a circular saw, exposures to silica dust produced by the cutting can be reduced by 80-90%. Later, NIOSH completed four field surveys where construction workers cut fiber cement siding. Results showed that exposure to silica dust was controlled below the NIOSH Recommended Exposure Limit for respirable crystalline silica when a regular shop vacuum was used.