History of the iron and steel industry in the United States


The US iron and steel industry has paralleled the industry in other countries in technological developments. In the 1800s, the US switched from charcoal to coke in ore smelting, adopted the Bessemer process, and saw the rise of very large integrated steel mills. In the 20th century, the US industry successively adopted the open hearth furnace, then the basic oxygen steelmaking process. Since the American industry peaked in the 1940s and 1950s, the US industry has shifted to small mini-mills and specialty mills, using iron and steel scrap as feedstock, rather than iron ore.

Colonial

Iron manufacture before the 19th century required charcoal, and Britain's once-vast forests could no longer supply enough charcoal for the nation's increasing need for iron. By 1700, Britain was becoming increasingly dependent on iron imported from its sometimes-adversary Sweden. Britain looked to the seemingly limitless forests of its American colonies to supply Britain with iron. British investors started an iron furnace near Perryville, Maryland, which in 1718 started exporting iron back to Britain. That success prompted formation of more companies, which built numerous iron furnaces around Chesapeake Bay, supplied by bog iron ore, which was widespread. By 1751, Virginia and Maryland were exporting 2,950 tons of pig iron to Britain each year; at the time, British iron production was about 20,000 tons per year.
While the Chesapeake Bay furnaces were established for export, iron furnaces were established in the 1700s throughout the American colonies for domestic consumption. Iron furnaces were located along rivers to supply water power. Also required were forests for charcoal, iron ore, and limestone for flux. In addition, the furnace needed to be close to a major market or close to water transport.
British business interests were split on colonial iron: manufacturers appreciated the lower prices due to colonial imports, but the British iron and steel industry objected to the competition. Parliament compromised in the Iron Act of 1750, which eliminated the import duty on colonial pig iron, but barred the manufacture of steel or of iron plate in the colonies. The law was widely ignored by colonial governments.
By 1776, up to 80 iron furnaces throughout the American colonies were producing about as much iron as Britain itself. If one estimate of 30,000 tons of iron each year is accurate, then the newly formed United States was the world's third-largest iron producer, after Sweden and Russia.
Notable pre-19th-century iron furnaces in the US
NameLocationStart DateEnd Date
Boonton Iron WorksBoonton, New Jerseycirca 17701911
Catoctin FurnaceCatoctin Furnace, Maryland17741903
Falling Creek IronworksChesterfield County, Virginia16221622
Furnace MountainLoudoun County, Virginiacirca 1790circa 1870
Hunter's IronworksFalmouth, Virginiacirca 17501782
Huntingdon FurnaceHuntingdon County, Pennsylvania1796circa 1880
Neabsco Iron WorksWoodbridge, Virginiacirca 1737
New Roxbury Ironworks SiteWoodstock, Connecticut1757
Patuxent Iron WorksAnne Arundel County, Maryland17051856
Principio FurnaceCecil County, Maryland17191925
Stirling Iron WorksMonroe, New York17611842
Taunton Iron WorksRaynham, Massachusetts16561876
Washington Iron FurnaceRocky Mount, Virginiacirca 1770

Early republic

Because wood for charcoal was available throughout the eastern states, iron smelters were located close to iron ore. Although the bog iron ores mined in colonial days were widespread, the deposits were also small, and quickly exhausted. In the late 1700s the iron furnaces moved away from the bog iron ore of the coastal swamps, to larger iron ore deposits further inland. Inland locations also allowed the furnaces to be closer to sources of limestone, which was used as a flux in iron smelting. The proximity to larger ore deposits favored larger, more permanent iron smelters.
Most US iron smelting before 1850 took place near iron deposits in eastern Pennsylvania, New York, and northern New Jersey. New Jersey's principal iron ore district, at Dover, supported iron smelters beginning in 1710. The Cornwall Iron Furnace in Pennsylvania was established next to an iron deposit. The Adirondack iron ore district of New York also supported iron smelters.
The movement away from charcoal in US iron smelting began in 1827, when a puddling furnace in Phoenixville, Pennsylvania started using anthracite coal. Blast furnaces continued to use only charcoal until about 1840, when coke from coal started replacing charcoal as the fuel and reducing agent. Coke has a higher crushing strength than charcoal, allowing larger smelting furnaces. Because iron and steel-making at the time consumed more coal than iron ore, the steel mills moved closer to the coal mines to minimize transportation costs. A problem of coke was that it carried impurities such as sulfur, which degraded the quality of the steel. Although coke quickly became the dominant fuel for iron-smelting, in 1884 charcoal was still used to make ten percent of iron and steel in the US. The use of charcoal for steelmaking survived in the US on a small scale until 1945.
The Lackawanna Valley in Pennsylvania was rich in anthracite coal and iron deposits. Brothers George W. Scranton and Seldon T. Scranton moved to the valley in 1840 and settled in the five-house town of Slocum's Hollow to establish an iron forge. The most common processes for creating blister steel and crucible steel were slow and extremely expensive. The Scrantons instead used the new "hot blast method," developed in Scotland in 1828. The hot blast method solved the problem of impurities from the coke, by burning them off. The Scrantons also experimented with anthracite to make steel, rather than charcoal or bituminous coal.
Notable early 19th-century iron furnaces in the US
NameLocationStart DateEnd Date
Bradys Bend Iron Company FurnacesArmstrong County, Pennsylvania18401873
Catherine FurnaceNewport, Page County, Virginia18361885
Curtin VillageCentre County, Pennsylvania18101921
Elizabeth FurnaceFort Valley, Virginia18361888
Georges Creek Coal and Iron CompanyLonaconing, Maryland18371855
Isabella FurnaceChester County, Pennsylvania18351894
Joppa Iron WorksBaltimore County, Marylandcirca 1817circa 1865
Longdale Furnace Historic DistrictClifton Forge, Virginia1827
Mount Savage Iron WorksMount Savage, Maryland1837circa 1870
Nassawango Iron Furnace SiteSnow Hill, Maryland18301849
Richmond Furnace Historical and Archeological DistrictRichmond, Massachusetts18291923
Roaring Run FurnaceEagle Rock, Virginia1832
Scranton Iron FurnacesScranton, Pennsylvania18481902
Tredegar Iron WorksRichmond, Virginia1837circa 1950

Pittsburgh

The replacement of charcoal with coal in the steel-making process revolutionized the industry, and tied steelmaking to coal-mining areas. In the 1800s, making a ton of steel required a greater weight of coal than iron ore. Therefore, it was more economical to locate closer to the coal mines. Pittsburgh, surrounded by large coal deposits and at the junction of three navigable rivers, was an ideal location for steelmaking.

Great Lakes ports

The tremendous iron ore deposits around Lake Superior were located far from coal deposits, and so were shipped to ports on the southern Great Lakes that were closer to the coal mines of Pennsylvania, Ohio, Indiana, and Illinois. Large integrated steel mills were built in Chicago, Detroit, Gary, Cleveland, and Buffalo, to handle the Lake Superior ore.
Cleveland's first blast furnace was built in 1859. In 1860, the steel mill employed 374 workers. By 1880, Cleveland was a major steel producer, with ten steel mills and 3,000 steelworkers.
The city of Gary, Indiana was founded in 1906 by United States Steel Corporation to serve the Gary Works.
The Lackawanna Steel Company built a large integrated steel works near Buffalo, which began producing steel from Lake Superior ore in 1903. The company had made steel in Scranton, Pennsylvania since 1840, but moved to provide easier access to iron ore, and in an unsuccessful attempt to avoid labor troubles.

Birmingham, Alabama

Birmingham, Alabama became a major steel producer in the late 1800s, using locally mined coal and iron ore. The iron ore was mined from the Clinton Formation of Silurian age.
Notable defunct late 19th-century iron and steel furnaces in the US
NameOwnersLocationStart DateEnd Date
Antrim Iron CompanyMancelona, Michigan18861945
Bellefonte FurnaceBellefonte, Pennsylvania18881910
Bethlehem WorksBethlehem SteelBethlehem, Pennsylvania18571995
Brierfield FurnaceBrierfield, Alabama18611894
Callie FurnaceGlen Wilton, Virginiacirca 18731884
Cornwall FurnaceCedar Bluff, Alabamacirca 18621874
Endor Iron FurnaceCumnock, North Carolina18611971
Fayette Historic State ParkFayette, Michigan18671891
Homestead Steel WorksCarnegie Steel, US SteelHomestead, Pennsylvania18811986
Janney Furnace ParkOhatchee, Alabama18631864
Nittany FurnaceCentre County, Pennsylvania18881911
Oregon Iron CompanyLake Oswego, Oregon18671893
Sloss FurnaceBirmingham, Alabama18821971
South WorksUS SteelChicago, Illinois18571992
Sparrows Point, MarylandBethlehem SteelBaltimore County, Maryland18892012

World War II and after

As the only major steel maker not harmed during the war, the United States iron and steel industry reached its maximum world importance during and just after World War II. In 1945, the US produced 67% of the world's pig iron, and 72% of the steel. By comparison, 2014 percentages were 2.4% of the pig iron, and 5.3% of the steel production.
Although US iron and steel output continued to grow overall through the 1950s and 1960s, the world steel industry grew much faster, and the US share of world production shrank. In the 1960s, the US became a major importer of steel, mostly from Japan.

Contraction: 1979-1984

US production of iron and steel peaked in 1973, when the US industry produced a combined total of 229 million metric tons of iron and steel. But US iron and steel production dropped drastically during the recession of the late 1970s and early 1980s. From a combined iron and steel production of 203 million tons in 1979, US output fell almost in half, to 107 million tons in 1982. Some steel companies declared bankruptcy, and many permanently closed steelmaking plants. By 1989, US combined iron and steel production recovered to 142 million tons, a much lower level than in the 1960s and 1970s.
The causes of the sudden decline are disputed. Among the many causes alleged have been: dumping of foreign imports below cost, high labor costs, poor management, unfavorable tax policies, and costs of environmental controls. One recent study found that hypotheses based on declining domestic production cannot explain the magnitude of the decline in employment, as shipments of domestic steel products in 2005 were similar to the level of the early 1960s, whereas employment in the domestic sector had plummeted by approximately 75% over the same time period. Instead, the majority of the losses could be accounted for by rising productivity, principally through technological efficiencies and the shift from traditional steel plants to mini mills.
Cleveland had nine integrated steel mills in the 1970s. US Steel closed one mill in 1979, then shut down its six remaining Cleveland mills in 1984. Cleveland's two remaining steel producers, Republic Steel and Jones & Laughlin, merged to form LTV Steel in June 1984. LTV Steel declared bankruptcy in 2000. The operation, on both sides of the Cuyahoga River, is Cleveland's last remaining integrated steel mill, now owned by Arcelor Mittal.

Transformation

The number of integrated steel mills has continued to decline, and in 2014, only 11 integrated mills were operating in the US. Most of the steel produced has been by the growing number of mini-mills, also called specialty mills, which in 2014 numbered 113. In 1981, mini-mills produced an estimated 15% of US steel. Since 2002, steel produced by electric arc furnace, the process used by the mini-mills, has produced more than half the steel made in the US. Many companies operating integrated mills also have mini-mills.
A number of bankruptcies and acquisitions between 2000 and 2014 reversed the trend of industry fragmentation. In 2000, the top three steelmakers had 28% of the steelmaking capacity, and the top ten had 58%. By 2014, the top three accounted for 56% of the steel capacity, and the top ten 87%.
Notable defunct 20th-century steel furnaces in the US
NameOwnersLocationStart DateEnd Date
Duluth WorksUS SteelDuluth, Minnesota19151987
Fontana blast furnaceKaiser SteelFontana, California1942circa 1982
Geneva Steel millUS SteelVineyard, Utah19442001

U.S. Labor