Litharge


Litharge + argyros is one of the natural mineral forms of lead oxide, PbO. Litharge is a secondary mineral which forms from the oxidation of galena ores. It forms as coatings and encrustations with internal tetragonal crystal structure. It is dimorphous with the orthorhombic form massicot. It forms soft, red, greasy-appearing crusts with a very high specific gravity of 9.14–9.35. PbO may be prepared by heating lead metal in air at approximately 600 °C. At this temperature it is also the end product of oxidation of other lead oxides in air. This is often done with a set of bellows pumping air over molten lead and causing the oxidized product to slip or fall off the top into a receptacle, where it quickly solidifies in minute scales.

Historical terminology

Historically, the term "litharge" has been combined to refer to other similar substances. For example, litharge of gold is litharge mixed with red lead, giving it a red color; litharge of bismuth is a similar result of the oxidation of bismuth; litharge of silver is litharge that comes as a by-product of separating silver from lead, in fact litharge originally meant the mineral residue from silver refining. The term has also been used as a synonym for white lead or red lead.

Litharge smelting

According to Probert, "silver ore, litharge flux and charcoal were mixed and smelted in very small clay and stone furnaces. Resulting silver-bearing lead bullion was later refined in a second furnace which yielded fine silver, and litharge skimmings which were used again."