Overglaze decoration, overglaze enamelling or on-glaze decoration is a method of decorating pottery, most often porcelain, where the coloured decoration is applied on top of the already fired and glazed surface, and then fixed in a second firing at a relatively low temperature, often in a muffle kiln. It is often described as producing "enamelled" decoration. The colours fuse on to the glaze, so the decoration becomes durable. This decorative firing is usually done at a lower temperature which allows for a more varied and vidid palette of colours, using pigments which will not colour correctly at the high temperature necessary to fire the porcelain body. Historically, a relatively narrow range of colours could be achieved with underglaze decoration, where the coloured pattern is applied before glazing, notably the cobalt blue of blue and white porcelain. Many historical styles, for example mina'i ware, Imari ware, Chinese doucai and wucai, combine the two types of decoration. In such cases the first firing for the body, underglaze decoration and glaze is followed by the second firing after the overglaze enamels have been applied. The technique essentially uses powdered glass mixed with coloured pigments, and is the application of vitreous enamel to pottery; enamelled glass is very similar but on glass. Both these latter two are essentially painting techniques, and have been since they began. In contrast, on metal painting in enamel arrived very late, long after techniques such as cloisonné, where thin wires are applied to form raised barriers, which contain areas of enamel, and champlevé, where the metal surface is sunk to form areas where the enamel is poured.
History
Enamel was used in jewellery, applied to metal, from very early on - there are examples in the Tomb of Tutankhamun of c. 1325 BC. Enamel was also used to decorate glass by the time of the Roman Empire. Applied to pottery, it is first seen in Persian mina'i ware from the late 12th century, using a group of seven main colours. Presumably the potters learnt the technique from glassmakers. Slightly later it appeared in Chinese ceramics in Cizhou stoneware from as early as the 13th century, with use on porcelain following within a century, though it did not become predominant until later, and the full possibilities were not realized until the 17th century. Some techniques use thin metal leaf, including mina'i ware as well as the more usual pigments, which are typically applied in a liquid or paste form, painted by brush, or using stencils or transfer printing. The technique was also developing in European porcelain, and some faience, during the 18th century, and there appears to have been some influence in both directions between Asia and Europe. From about 1770 to the mid 20th century it was the dominant decorative technique in expensive pottery, mostly porcelain, made in Europe, East Asia, and North America. In 18th-century England, where the technique was developed, the earliest forms of transfer printing on pottery, for example by Sadler & Green in Liverpool, were overglaze, although by the end of the century it was normal to print as underglaze. Today overglaze decoration is much less commonly used, other than in traditionalist wares, as the range of colours available in underglaze has greatly expanded.
Muffle kilns
The kiln used for the second firing is usually called a muffle kiln in Europe; like other types of muffle furnaces the design isolates the objects from the flames producing the heat. For historical overglaze enamels the kiln was generally far smaller than that for the main firing, and produced firing temperatures in the approximate range of 750 to 950 °C, depending on the colours used. Typically, wares were fired for between five and twelve hours and then cooled over twelve hours.