Spaced armour
with two or more plates spaced a distance apart falls under the category of spaced armour. Spaced armour can be sloped or unsloped. When sloped, it reduces the penetrating power of bullets and solid shot, as after penetrating each plate projectiles tend to tumble, deflect, deform, or disintegrate; spaced armor that is not sloped is generally designed to provide protection from explosive projectiles, which detonate before reaching the primary armor. Spaced armour is used on armoured military vehicles such as tanks and combat bulldozers. In a less common application, it is used in some spacecraft that use Whipple shields.
Against kinetic penetrators
The first spaced armors were used on iron warships from mid 19th century. Between the thin outer armor of various less important parts and the thick main armor were constructed storage spaces, coal or oil bunkers, and so on. Some ships had thicker outer and thinner inner layers in order to lower the damage caused by the penetrating round. From 1900 some cruisers and battleships were built with modern spaced armor, where the outer thin layer was intended only to damage the projectiles.Torpedo bulkheads also serve as a special form of spaced armor for naval vessels.
Tank spaced armour has been fielded since the First World War, when it was fitted to the French Schneider CA1 and Saint-Chamond tanks. The late variants of Panzer III had frontal spaced armour. A 20 mm thick face-hardened steel layer were in front of the 50 mm thick main armor. Impacted projectiles were physically damaged by the plate, so the main armor could withstand much greater hits. Due to lack of materials, German industry eventually switched to Rolled homogeneous armour, which is less effective and due to the slower production process, the technique was not widespread on German tanks.
It is important in designing of integral spaced armor that each layer should be thick enough to cause adequate damage to the projectile or jet. So the thickness of every layer should reach roughly the half of the diameter of projectile expected to impact.
Many World War II-era German tanks utilized armored skirts to make their thinner side armor more resistant to anti-tank rifle fire. Contrary to popular belief the German Schürzen were designed against kinetic projectiles. The effectiveness of conventional AP projectiles was significantly reduced if they broke through a thin plate or dense wire net, because the projectiles become unstable in their trajectory and their tip would also be damaged. This method was very effective against contemporary light anti-tank weapons, like the Soviet PTRD-41 and M1937, the British 6-pounder, and the US 37mm gun.
Some armored vehicles used nets of wooden logs at a certain distance from the hull as makeshift spaced armour in order to protect the vehicle from magnetic mines, thrown shaped charges and grenades, and occasionally suicidal methods. This method occurred on US Sherman and Soviet T-34 vehicles, among others.
Against High Explosive Anti Tank rounds
Most of Cold war spaced armors designed against medium-to-low caliber kinetic munitions,, especially vehicle side skirts. Most of them made of RHA plates, or thick reinforced rubbers, and worked in the same way of WW2-era ones.This light armour also detonates explosive warheads prematurely. High Explosive Anti Tank-type warheads use a focused hypervelocity jet of copper or steel to penetrate armour. To be effective, HEAT warheads must detonate at a specific distance from the target's primary armour to ensure maximum penetration. Thus early detonation greatly reduces the penetration of HEAT ammunition. This requires a distance of 1.2 meters even for an early 100mm projectile, thus conventional skirts are effective against HEAT only at very low angle of incidence.
The use of add-on spaced armour skirts can sometimes have the opposite effect and increase the penetration of some shaped charge warheads. Due to constraints in the length of projectiles, some designs intentionally detonate closer than the optimum distance. In such cases, the skirting effectively increases the distance between the armor and the target, and the warhead detonates closer to its optimum stand-off.
To increase effectiveness of skirts against HEAT weapons some mid-cold-war tanks had gill-style armor. It contained a few short skirts on the side of the vehicle which are opened in open terrain at an angle of 30-45° increasing the space between the armor and the plate. It was effective, but easily detached from the vehicle so it did not spread widely.
A special version of reactive spaced armor is slat armor. It uses the own power of the impacting projectile to destroy it. Steel slats placed at a specified distances have a 50-60% chance of breaking the RPG-7's warhead so no cumulative beam can be formed. It also provides some protection against thrown grenades.
In response to increasingly effective HEAT, HESH and APFSDS warheads, integral spaced armour was reintroduced in the 1960s on the German Leopard 1 and later the Merkava. Hollow spaces between plates allow increase the distance a projectile must travel to reach the interior of a vehicle. Sometimes the interior surfaces of these hollow cavities are sloped, presenting angles to the anticipated path of the shaped charge's jet or kinetic penetrator to further dissipate their power. The two layered spaced RHA armors were highly effective against early steel and tungsten APFSDS munitions, because the rod was severely damaged by penetrating the first layer and was thus ineffective on the inner armor. Therefore, a much thinner total steel thickness and weight was enough against a specific projectile. For example, a given weight of armour can be distributed in 2 layers 15 cm thick instead of a single 30 cm layer, giving much better protection against HESH and APDS munitions, but their effect on shaped charges was limited. So military researchers tried to increase the efficiency of spaced armour by changing the used materials and increasing the number of layers, from the early sixties.
Composite spaced armours
Multilayer spaced armors, which also uses special materials, are transition to composite armor, most of the latter are also partially spaced armor.In case of Leopard1A3 and later variants the outer layer of spaced armor was hardened steel and the space was filled by elastomer, thus the effectiveness of shattering effect of the outer layer against APFSDS were outstanding, and the protection against early HEAT warheads were increased too. The BDD add-on armor of T-55 and T-62 series based on the same effect, but it had multiple layers within elastomer, therefore it roughly doubled the frontal protection of these tanks against APDS and HEAT weapons, and make the areas of add-on immune against HESH rounds. In T-64 and early T-72 and T-80 used stakloplastika as filling in the frontal upper glacis spaced armor. This plastic was effective in lowering the concentration of the jet of shaped charges and in destabilizing kinetic penetrators.
Hardened steel plates has become commonplace for outer part of spaced armors from '80s not only on tanks but also on APCs and IFVs. With these add-on armors even the APC's thin armor is sufficient against kinetic bullets of 12.7 and 14.5 calibers and also provides some protection against IEDs.
The increase of the number of layers in spaced armor increases the physical damage and destabilization of jets and kinetic penetrators, so it is common in more modern armor to use successive layers alternating between softer and harder layers. With multiple layers the likelihood of bounce in case of kinetic projectiles is also increasing, and SC jets loss from their material when come through between layers with different density and their performance lowered due to the effects pressure and velocity changes on their concentration. Thus later T-72B and T-90 armors used 7 layered spaced armor in order to achieve much stronger protection in cost of minimum weight increase.
The more advanced late cold war tanks were given multi-layer skirts, in which passive effects significantly reduced the effectiveness of HEAT ammunition. At the same time, these elements are already heavy and have considerable thickness, which increase the size and weight of the vehicle and make maintenance difficult. Russian and some western tanks carries explosive-reactive armor blocks in order to increase effectiveness of spaced armors, and main frontal armor.
Almost all of modern western and Japanese and most of soviet tanks use some kind of spaced armors on fronts and sides. Side panels of superstructure usually contain fuel, batteries and other less vital elements or munition of secondary weapons, because they also reduce the effectiveness of penetrating projectiles. In most important areas the cavity of spaced armor contain composite panels. From 80's most of western tanks has composite armor blocks on the frontal part of skirts made of hardened steel or NERA armor. Most of modern MBTs have NERA armor in their spaced armors which supplemented with inner ceramic armor and spall liners in some cases. In contrast, Soviet tanks were initially made with ceramic inserts and NERA-style inserts have spread in the upgraded versions of their vehicles later. More detail in composite armour.
Nowadays composite spaced armors with hardened steel outer layer are becoming more common on most advanced light battle tanks and IFVs.
Materials
As designs became more specialized, more and more materials were used. the most important are:Elastomers
Some modern main battle tanks and IFVs carry rubber or steel skirts to protect their relatively fragile suspension and lower side armor and lower glacis, often combining the two. Some elastomer fillings behave like spaced armor, where the elastic layer effectively lowers the concentration of the jet of HEAT warheads. Leopard 1A3 and 1A4 and add-on armors of T-55 and T-62 used dense polystyrene filling in order to increasing the effectiveness of spaced armors. The early second generation Russian MBTs used dense glass-fiber reinforced pressured plastic as filling in the frontal upper glacis spaced armor which is even more effective than the pure elastomer.NERA armors also use elastomers pressed between two or three sheets steel or aluminium layers, it acts as ERA armors with lesser effectiveness, but is not destroyed during operation, so it can hold multiple hits in same place. Most of modern MBTs use some NERA layer within their spaced armour, or as outer layer.
Hardened steel
Whereas normal armour must compromise between hardness and ductility, spaced armour can be constructed from plates with differing material properties to increase effectiveness against kinetic energy penetrators. Most of Cold war and modern spaced armors use rolled homogeneous armor as inner and a thin face-hardened, semi-hardened steel plate as outer layer. The thin, but very hard outer layer acts as burster and shatter plate which allow to design main armor much thinner with the same protection level The most advanced designs use triple- or high-hardened steels. In some cases aluminium is added to hardened steel armor as softer inter-layer in order to destabilising the projectiles and HEAT jets by density changes.The Leopard 2 utilizes a slanted first armour stage, a specially hardened second stage and a softer, high ductility third stage. The disturber is designed to either entirely deflect or manipulate the direction of incoming kinetic energy penetrators. If penetration does occur, the projectile is then shattered and fragmented when striking the disrupter. Assuming the first two stages work properly, the absorber stage captures spalling and fragments.