Solid oxide electrolyzer cell
A solid oxide electrolyzer cell is a solid oxide fuel cell that runs in regenerative mode to achieve the electrolysis of water by using a solid oxide, or ceramic, electrolyte to produce hydrogen gas and oxygen.
The production of pure hydrogen is compelling because it is a clean fuel that can be stored easily, thus making it a potential alternative to batteries, which have a low storage capacity and create high amounts of waste materials. Electrolysis is currently the most promising method of hydrogen production from water due to high efficiency of conversion and relatively low required energy input when compared to thermochemical and photocatalytic methods.
Principle
Solid oxide electrolyzer cells operate at temperatures which allow high-temperature electrolysis to occur, typically between 500 and 850 °C. These operating temperatures are similar to those conditions for an SOFC. The net cell reaction yields hydrogen and oxygen gases. The reactions for one mole of water are shown below, with oxidation of water occurring at the anode and reduction of water occurring at the cathode.Anode: O2− → 1/2O2 + 2e−
Cathode: H2O + 2e− → H2 + O2−
Net Reaction: H2O → H2 + 1/2O2
Electrolysis of water at 298 K requires 285.83 kJ of energy per mole in order to occur, and the reaction is increasingly endothermic with increasing temperature. However, the energy demand may be reduced due to the Joule heating of an electrolysis cell, which may be utilized in the water splitting process at high temperatures. Research is ongoing to add heat from external heat sources such as concentrating solar thermal collectors and geothermal sources.
Operation
The general function of the electrolyse cell is to split water in the form of steam into pure H2 and O2. Steam is fed into the porous cathode. When a voltage is applied, the steam moves to the cathode-electrolyte interface and is reduced to form pure H2 and oxygen ions. The hydrogen gas then diffuses back up through the cathode and is collected at its surface as hydrogen fuel, while the oxygen ions are conducted through the dense electrolyte. The electrolyte must be dense enough that the steam and hydrogen gas cannot diffuse through and lead to the recombination of the H2 and O2−. At the electrolyte-anode interface, the oxygen ions are oxidized to form pure oxygen gas, which is collected at the surface of the anode.Materials
Solid oxide electrolyzer cells follow the same construction of a solid-oxide fuel cell, consisting of a fuel electrode, an oxygen electrode and a solid-oxide electrolyte.Electrolyte
The most common electrolyte, again similar to solid-oxide fuel cells, is a dense ionic conductor consisting of ZrO2 doped with 8 mol % Y2O3. Zirconia dioxide is used because of its high strength, high melting temperature and excellent corrosion resistance. Y2O3 is added to mitigate the phase transition from the tetragonal to the monoclinic phase on rapid cooling, which can lead to cracks and decrease the conductive properties of the electrolyte by causing scattering. Some other common choices for SOEC are Scandia stabilized zirconia, ceria based electrolytes or lanthanum gallate materials. Despite the material similarity to solid oxide fuel cells, the operating conditions are different, leading to issues such as high steam concentrations at the fuel electrode and high oxygen partial pressures at the electrolyte/oxygen electrode interface. A recent study found that periodic cycling a cell between electrolyzer and fuel cell modes reduced the oxygen partial pressure build up and drastically increased the lifetime of the electrolyzer cell.Fuel Electrode (Cathode)
The most common fuel electrode material is a Ni doped YSZ, however, high steam partial pressures and low hydrogen partial pressures at the Ni-YSZ interface caused oxidation of the nickel and lead to irreversible degradation. Perovskite-type lanthanum strontium manganese is also commonly used as a cathode material. Recent studies have found that doping LSM with scandium to form LSMS promotes mobility of oxide ions in the cathode, increasing reduction kinetics at the interface with the electrolyte and thus leading to higher performance at low temperatures than traditional LSM cells. However, further development of the sintering process parameters is required to prevent precipitation of scandium oxide into the LSM lattice. These precipitate particles are problematic because they can impede electron and ion conduction. In particular, the processing temperature and concentration of scandium in the LSM latice are being researched to optimize the properties of the LSMS cathode. New materials are being researched such as lanthanum strontium manganese chromate, which has proven to be more stable under electrolysis conditions. LSCM has high redox stability, which is crucial especially at the interface with the electrolyte. Scandium-doped LCSM is also being researched as a cathode material due to its high ionic conductivity. However, the rare-earth element introduces a significant materials cost and was found to cause a slight decrease in overall mixed conductivity. Nonetheless, LCSMS materials have demonstrated high efficiency at temperatures as low as 700 °C.Oxygen Electrode (Anode)
Lanthanum strontium manganate is the most common oxygen electrode material. LSM offers high performance under electrolysis conditions due to generation of oxygen vacancies under anodic polarization that aid oxygen diffusion. In addition, impregnating LSM electrode with GDC nanoparticles was found to increase cell lifetime by preventing delamination at the electrode/electrolyte interface. The exact mechanism by how this happen needs to be explore further. In a 2010 study, it was found that neodymium nickelate as an anode material provided 1.7 times the current density of typical LSM anodes when integrated into a commercial SOEC and operated at 700 °C, and approximately 4 times the current density when operated at 800 °C. The increased performance is postulated to be due to higher "overstoichimoetry" of oxygen in the neodymium nickelate, making it a successful conductor of both ions and electrons.Considerations
Advantages of solid oxide-based regenerative fuel cells include high efficiencies, as they are not limited by Carnot efficiency.Additional advantages include long-term stability, fuel flexibility, low emissions, and low operating costs. However, the greatest disadvantage is the high operating temperature, which results in long start-up times and break-in times. The high operating temperature also leads to mechanical compatibility issues such as thermal expansion mismatch and chemical stability issues such as diffusion between layers of material in the cell
In principle, the process of any fuel cell could be reversed, due to the inherent reversibility of chemical reactions.
However, a given fuel cell is usually optimized for operating in one mode and may not be built in such a way that it can be operated in reverse. Fuel cells operated backwards may not make very efficient systems unless they are constructed to do so such as in the case of solid oxide electrolyzer cells, high pressure electrolyzers, unitized regenerative fuel cells and regenerative fuel cells. However, current research is being conducted to investigate systems in which a solid oxide cell may be run in either direction efficiently.
Delamination
Fuel cells operated in electrolysis mode have been observed to degrade primarily due to anode delamination from the electrolyte. The delamination is a result of high oxygen partial pressure build up at the electrolyte-anode interface. Pores in the electrolyte-anode material act to confine high oxygen partial pressures inducing stress concentration in the surrounding material. The maximum stress induced can be expressed in terms of the internal oxygen pressure using the following equation from fracture mechanics:where c is the length of the crack or pore and is the radius of curvature of the crack or pore. If exceeds the theoretical strength of the material, the crack will propagate, macroscopically resulting in delamination.
Virkar et al. created a model to calculate the internal oxygen partial pressure from the oxygen partial pressure exposed to the electrodes and the electrolyte resistive properties. The internal pressure of oxygen at the electrolyte- anode interface was modelled as:
where is the oxygen partial pressure exposed to the oxygen electrode, is the area specific electronic resistance at the anode interface, is the area specific ionic resistance at the anode interface, is the applied voltage, is the Nernst potential, and are the overall electronic and ionic area specific resistances respectively, and and are the electric potentials at the anode surface and the anode electrolyte interface respectively.
In electrolysis mode > and >. Whether is greater than is dictated by whether or is greater than . The internal oxygen partial pressure is minimized by increasing the electronic resistance at the anode interface and decreasing the ionic resistance at anode interface.
Delamination of the anode from the electrolyte increases the resistance of the cell and necessitates higher operating voltages in order to maintain a stable current. Higher applied voltages increases the internal oxygen partial pressure, further exacerbating the degradation.
Applications
SOECs have possible application in fuel production, carbon dioxide recycling, and chemicals synthesis. In addition to the production of hydrogen and oxygen, an SOEC could be used to create syngas by electrolyzing water vapor and carbon dioxide.This conversion could be useful for energy generation and energy storage applications.
MIT will test the method on the Perseverance rover as a means to produce oxygen for both human sustenance and liquid oxygen rocket propellant.