Dental material


Dental products are specially fabricated materials, designed for use in dentistry. There are many different types of dental products, and their characteristics vary according to their intended purpose.

Temporary dressings

A temporary dressing is a dental filling which is not intended to last in the long term. They are interim materials which may have therapeutic properties. A common use of temporary dressing occurs if root canal therapy is carried out over more than one appointment. In between each visit, the pulp canal system must be protected from contamination from the oral cavity, and a temporary filling is placed in the access cavity. Examples include:
Dental cements are used most often to bond indirect restorations such as crowns to the natural tooth surface. Examples include:
Dental impressions are negative imprints of teeth and oral soft tissues from which a positive representation can be cast. They are used in prosthodontics, orthodontics, restorative dentistry, dental implantology and oral and maxillofacial surgery.
These two properties are essential because patients have varying soft-tissue undercuts. In order to obtain an accurate impression, a suitable property of impression material must be used. Impression materials are designed to be liquid or semi-solid when first mixed, then set hard in a few minutes, leaving imprints of oral structures.
Common dental impression materials include:
Historically these products were used as impression materials:
Dental lining materials are used during restorations of large cavities, and are placed between the remaining tooth structure and the restoration material. The purpose of this is to protect the dentinal tubules and the sensitive pulp, forming a barrier-like structure. After drilling the caries out of the tooth, the dentist applies a thin layer to the base of the tooth, followed by light curing. Another layer might be applied if the cavity is very large and deep.
There are many functions to dental lining materials, some of which are listed below:
Calcium Hydroxide
Calcium Hydroxide has a relatively low compressive strength and a viscous consistency making them difficult to apply to cavities in thick sections, a common technique used to overcome this issue would be to apply a thin sub-lining of a calcium hydroxide lining and then building up with zinc phosphate prior to amalgam condensation.Generates a relatively high pH environment around area surrounding the cement due to calcium hydroxide leaking out thus making it bactericidal. It also has a unique effect of initiating calcification and stimulating the formation of secondary dentine due to an irritation effect of the pulp tissues by the cement. It is also radio-opaque and acts as a good thermal and electrical insulation. However, due to its low compressive strength it is unable to withstand amalgam packing thus a strong cement base material should be placed above it to counter this. Calcium silicate-based liners have become alternatives to calcium hydroxide and a preferred material among practitioners for its bioactive and sealing properties; the material triggers a biological response and results in formation of bonding with the tissue. Commonly used as pulp capping agents and lining materials for silicate and resin-based filling materials.
It is usually supplied as 2 pastes, a glycol salicylate and another paste containing Zinc Oxide with Calcium Hydroxide. On mixing a chelate compounds are formed. Light activated versions are also available which contains polymersiation activators, hydroexyethyl methacrylate, dimethacrylate which when light activated will result in a light activated polymerization reaction of a modified methacrylate monomer.
Polycarboxylate cement
Polycarboxylate cement have decent compressive strength to resists amalgam condensation and are acidic but less acidic then phosphate cements due to it having a higher molecular weight and polyacrylic acid being a weaker acid than phosphoric acid.They also form a strong bond with dentine and enamel allowing it to form a coronal seal. In addition it is an electrical and thermal insulator while also releasing fluoride rendering it bacteriostatic, furthermore it being radio-opaque makes it an excellent lining material.
Care has to be taken in handling such material as it has a strong bond with stainless steel instruments once it sets.
Commonly used as luting agents or as cavity base materials, however they tend to be rubbery during its setting reaction and adhere to stainless steel instruments thus most operators would prefer not to use them in deep cavities.
It is usually supplied as a power containing Zinc Oxide and a liquid containing aqueous Polyacrylic acid. The reaction consists of an acid base reaction with Zinc oxide reacting with the acid groups in polyacid to form a reaction product of unreacted zinc oxide cores bound by a salt matrix with polyacrylic acid chains cross linking with zinc ions.
Glass ionomer
It has the strongest compressive and tensile strength out of all the linings, thus it can withstand amalgam condensation in high stress bearing areas such as class II cavities. GI is used as a lining material as it is very compatible with most restorative materials, insulates thermally and electrically and adheres to enamel and dentine. Lining GI contains glass of smaller particle sizes in comparison to its adhesive restorative mix to allow formation of a thinner film. Some variations are also radiopaque which makes it good for X ray cavity detection. In addition, GI is bacteriostatic due to its fluoride release from un-reacted glass cores.
GIs are usually used as a lining material for composite resins or as luting agents for orthodontic bands.
The reaction is an acid-base reaction between silicate glass powder and polyacrylic acid. They come in a powder and liquid which are mixed on a pad or in compules which are for single usage and light cured with a LED light curing unit. Setting takes place by a combination of both an acid based reaction and chemically activated polymerization, light cured versions contain a photo-initiator usually camphorquinone and an amide.
Zinc oxide eugenol
Zinc oxide eugenol has the lowest compressive and tensile strength in relative to the rest of the liners thus this lining should be limited to small or non stress bearing areas such as Class V cavities. This cavity lining is often used with a high strength base to provide strength, rigidity and thermal insulation. Zinc oxide eugenol can be used as linings in deep cavities without causing harm to the pulp, due to its obtundant effect on the pulp as well as its bactericidal properties due to Zinc. However eugenol may have an effect on resin based filling materials as it interferes with the polymerization and occasionally causes discoloration, thus caution should be taken when using both in tandem. It is also radio-opaque allowing fillings to be visible by X-rays.
Zinc oxide eugenol is usually used as a temporary filling/luting agent due to its low compressive strength and thus easily removed or as a lining for amalgam as it is incompatible with composites resins.
It is supplied as a two paste system. Equal length of 2 pastes are dispensed into a paper pad and mixed.
AgentAdvantagesDisadvantages
Calcium Hydroxide
  • Alkaline nature promotes anti-bacterial atmosphere
  • Therapeutic effect for dentinal tubules
  • Low thermal conductivity can provide thermal insulation
  • Radiopaque
  • Thermal and electrical insulator
  • Good restorative material compatibility
  • Soluble to oral fluids thus restricted to dentine coverage only
  • Viscous consistency making it difficult to apply to cavities in thick sections\
  • Low compressive strength need a second layer of strong cement base above it
    • Polycarboxylate cement
  • Decent compressive and tensile strength
  • Radiopaque
  • Bacteriostatic due to fluoride release
  • Adhesive thus coronal seal
  • Compatible with most restorative materials
  • Thermal and electrical insulator
  • Mildly acidic thus a mild irritant
  • Hard to handle due to strong bond with stainless steel instruments
  • Rubbery during setting reaction thus hard to manipulate in deep cavities
    • Zinc Oxide Eugenol
  • Can be used as a temporary filling or lining as it is easy to remove even after set
  • Bactericidal due to Zinc
  • Thermal and electrical insulator
  • Radioaque due to Zinc
  • Obtundant
  • Lowest compressive and tensile strength of all linings only can be used on areas with small or non stress
  • Incompatible with resin composites due to polymerization interference
  • Non adhesive thus no coronal seal
    • Glass ionomer
  • Very high compressive and tensile strength
  • Radiopaque
  • Very adhesive to enamel and dentine thus don't need a bonding agent
  • Bacteriosatic due to fluoride release
  • Adhesive thus coronal seal
  • Good compatibility with restorative materials
  • Thermal and electrical insulator
  • Mildly acidic thus a mild irritant
  • Remain acidic for some time after mixing
  • Not an obtundant

    • Restorative materials

    Dental restorative materials are used to replace tooth structure loss, usually due to dental caries, but also tooth wear and dental trauma. On other occasions, such materials may be used for cosmetic purposes to alter the appearance of an individual's teeth.
    There are many challenges for the physical properties of the ideal dental restorative material. The goal of research and development in restorative materials is to develop the ideal restorative material. The ideal restorative material would be identical to natural tooth structure in strength, adherence, and appearance. The properties of an ideal filling material can be divided into four categories: physical properties, biocompatibility, aesthetics and application.
    Direct restorations are ones which are placed directly into a cavity on a tooth, and shaped to fit. The chemistry of the setting reaction for direct restorative materials is designed to be more biologically compatible. Heat and byproducts generated cannot damage the tooth or patient, since the reaction needs to take place while in contact with the tooth during restoration. This ultimately limits the strength of the materials, since harder materials need more energy to manipulate.
    The type of filling material used has a minor effect on how long they last. The majority of clinical studies indicate the annual failure rates are between 1% and 3% with tooth colored fillings on back teeth. Note that root canaled treated teeth have AFR's between 2% and 12%. The main reasons for failure are cavities that occur around the filling and fracture of the real tooth. These are related to personal cavity risk and factors like grinding teeth.

    Amalgam

    is a metallic filling material composed from a mixture of mercury and powdered alloy made mostly of silver, tin, zinc and copper, commonly called the amalgam alloy. Amalgam does not adhere to tooth structure without the aid of cements or use of techniques which lock in the filling, using the same principles as a dovetail joint.
    Amalgam is still used extensively in many parts of the world because of its cost effectiveness, superior strength and longevity. However, the metallic colour is not aesthetically pleasing and tooth coloured alternatives are continually emerging with increasingly comparable properties. Due to the known toxicity of the element mercury, there is some controversy about the use of amalgams. The Swedish government banned the use of mercury amalgam in June 2009.
    Research has shown that, while amalgam use is controversial and may increase mercury levels in the human body, these levels are below safety threshold levels established by the WHO and the EPA. However, there are certain subpopulations who, due to inherited genetic variabilities, exhibit sensitivity to mercury levels lower than these threshold levels. These particular individuals may experience adverse effects caused by amalgam restoration. These include myriad neural defects, mainly caused by impaired neurotransmitter processing.

    Composite resin

    Composite resin fillings are a mixture of powdered glass and plastic resin, and can be made to resemble the appearance of the natural tooth. Although cosmetically superior to amalgam fillings, composite resin fillings are usually more expensive. Bis-GMA based resins contain Bisphenol A, a known endocrine disrupter chemical, and may contribute to the development of breast cancer. However, it has been demonstrated that the extremely low levels of bis-GMA released by composite restorations do not cause a significant increase in markers of renal injury, when compared to amalgam restorations. That is, there is no added risk of renal or endocrine injury in choosing composite restorations over amalgams. PEX-based materials do not contain Bisphenol A and are the least cytotoxic material available.
    Most modern composite resins are light-cured photopolymers, meaning that they harden with light exposure. They can then be polished to achieve maximum aesthetic results. Composite resins experience a very small amount of shrinkage upon curing, causing the material to pull away from the walls of the cavity preparation. This makes the tooth slightly more vulnerable to microleakage and recurrent decay. Microleakage can be minimized or eliminated by utilizing proper handling techniques and appropriate material selection.
    In some circumstances, less tooth structure can be removed compared to preparation for other dental materials such as amalgam and many of the indirect methods of restoration. This is because composite resins bind to enamel via a micromechanical bond. As conservation of tooth structure is a key ingredient in tooth preservation, many dentists prefer placing materials like composite instead of amalgam fillings whenever possible.
    Generally, composite fillings are used to fill a carious lesion involving highly visible areas or when conservation of tooth structure is a top priority.
    The bond of composite resin to tooth, is especially affected by moisture contamination and cleanliness of the prepared surface. Other materials can be selected when restoring teeth where moisture control techniques are not effective.

    Glass ionomer cement

    The concept of using "smart" materials in dentistry has attracted a lot of attention in recent years. Conventional glass-ionomer cements have a large number of applications in dentistry. They are biocompatible with the dental pulp to some extent.
    Clinically, this material was initially used as a biomaterial to replace the lost osseous tissues in the human body.
    These fillings are a mixture of glass and an organic acid. Although they are tooth-colored, glass ionomers vary in translucency. Although glass ionomers can be used to achieve an aesthetic result, their aesthetic potential does not measure up to that provided by composite resins.
    The cavity preparation of a glass ionomer filling is the same as a composite resin. However, one of the advantages of GI compared to other restorative materials is that they can be placed in cavities without any need for bonding agents.
    Conventional glass ionomers are chemically set via an acid-base reaction. Upon mixing of the material components, there is no light cure needed to harden the material once placed in the cavity preparation. After the initial set, glass ionomers still need time to fully set and harden.
    Advantages:
    1. Glass ionomer can be placed in cavities without any need for bonding agents.
    2. They are not subject to shrinkage and microleakage, as the bonding mechanism is an acid-base reaction and not a polymerization reaction.(GICs do not undergo great dimensional changes in a moist environment in response to heat or cold and it appears heating results only in water movement within the structure of the material. These exhibit shrinkage in a dry environment at temperature higher than 50C, which is similar to the behavior of dentin.
    3. Glass ionomers contain and release fluoride, which is important to preventing carious lesions. Furthermore, as glass ionomers release their fluoride, they can be "recharged" by the use of fluoride-containing toothpaste. Hence, they can be used as a treatment modality for patients who are at high risk for caries. Newer formulations of glass ionomers that contain light-cured resins can achieve a greater aesthetic result, but do not release fluoride as well as conventional glass ionomers.
    Disadvantages:
    The most important disadvantage is lack of adequate strength and toughness. In an attempt to improve the mechanical properties of the conventional GI, resin-modified ionomers have been marketed.
    GICs are usually weak after setting and are not stable in water; however, they become stronger with the progression of reactions and become more resistant to moisture.
    New generations: The aim is tissue regeneration and use of biomaterial in the form of a powder or solution is to induce local tissue repair. These bioactive materials release chemical agents in the form of dissolved ions or growth factors such as bone morphogenic protein, which stimulates activate cells.
    Glass ionomers are about as expensive as composite resin. The fillings do not wear as well as composite resin fillings. Still, they are generally considered good materials to use for root caries and for sealants.

    Resin modified glass-ionomer cement (RMGIC)

    A combination of glass-ionomer and composite resin, these fillings are a mixture of glass, an organic acid, and resin polymer that harden when light cured. The cost is similar to composite resin. It holds up better than glass ionomer, but not as well as composite resin, and is not recommended for biting surfaces of adult teeth, or when control of moisture cannot be achieved.
    Generally, resin modified glass-ionomer cements can achieve a better aesthetic result than conventional glass ionomers, but not as good as pure composites. It has its own setting reaction.

    Compomers

    Another combination of composite resin and glass ionomer technology, with focus lying towards the composite resin end of the spectrum. Compomers are essentially made up of filler, dimethacrylate monomer, difunctional resin, photo-activator and initiator, and hydrophilic monomers. The primary reason of the addition of filler is to decrease the proportion of resin and increase the mechanical strength besides improving the material's appearance.
    Although compomers have better mechanical and aesthetic properties than RMGIC, they have few disadvantages which limit their applications.
    Due to its relatively weaker mechanical properties, Compomers are unfit for stress-bearing restorations but can be used in the deciduous dentition where lower loads are anticipated.

    Cermets

    , also known as silver cermets, were created to improve the wear resistance and hardness of glass ionomer cements through the addition of silver. While the incorporation of silver achieved this, cermets have poorer aesthetics, appearing metallic rather than white. Cermets also have a similar compressive strength, flexural strength, and solubility as glass ionomer cements, some of the main limiting factors for both materials. Clinical studies have shown cermets perform poorly. All these disadvantages led to the decline in the use of this restorative material.
    Below is a summary of the advantages and disadvantages of dental cermets.
    Advantages:
    Disadvantages:
    Indirect restorations are ones where the tooth or teeth to receive the restoration are first prepared, then a dental impression is taken and sent to a dental technician who fabricates the restoration according to the dentist's prescription.
    Porcelain fillings are hard, but can cause wear on opposing teeth. They are brittle and are not always recommended for molar fillings. They are hard and rigid thus able to resist abrasion forces, are brittle due to surface irregularities, porosities, tendency to undergo static fatigue, and is good aesthetically as it mimics appearance of natural teeth due to various levels of shades. Porcelain materials can be strengthened by soaking fired material in molten salt to allow exchange of sodium and potassium ions on the surface as this successfully create compressive stresses on the outer layer, by controlling cooling after firing, and by the use of pure alumina inserts, a core of alumina or alumina powder, as they act as crack stoppers and are highly compatible to porcelain.
    Tooth colored dental composite materials are either used as direct filling or as construction material of an indirect inlay. It is usually cured by light.
    Nano-ceramic particles embedded in a resin matrix, are less brittle and therefore less likely to crack, or chip, than all-ceramic indirect fillings; they absorb the shock of chewing more like natural teeth, and more like resin or gold fillings, than do ceramic fillings; and at the same time more resistant to wear than all-resin indirect fillings. These are available in blocks for use with CAD-CAM systems.
    Gold fillings have excellent durability, wear well, and do not cause excessive wear to the opposing teeth, but they do conduct heat and cold, which can be irritating. There are two categories of gold fillings, cast gold fillings made with 14 or 18 kt gold, and gold foil made with pure 24 kt gold that is burnished layer by layer. For years, they have been considered the benchmark of restorative dental materials. Recent advances in dental porcelains and consumer focus on aesthetic results have caused demand for gold fillings to drop in favor of advanced composites and porcelain veneers and crowns. Gold fillings are sometimes quite expensive; yet, they do last a very long time—which can mean gold restorations are less costly and painful in the long run. It is not uncommon for a gold crown to last 30 years.

    Other historical fillings

    Lead fillings were used in the 18th century, but became unpopular in the 19th century because of their softness. This was before lead poisoning was understood.
    According to American Civil War-era dental handbooks from the mid-19th century, since the early 19th century metallic fillings had been used, made of lead, gold, tin, platinum, silver, aluminum, or amalgam. A pellet was rolled slightly larger than the cavity, condensed into place with instruments, then shaped and polished in the patient's mouth. The filling was usually left "high", with final condensation—"tamping down"—occurring while the patient chewed food. Gold foil was the most popular and preferred filling material during the Civil War. Tin and amalgam were also popular due to lower cost, but were held in lower regard.
    One survey of dental practices in the mid-19th century catalogued dental fillings found in the remains of seven Confederate soldiers from the U.S. Civil War; they were made of:
    Acrylics are used in the fabrication of dentures, artificial teeth, impression trays, maxillofacial / orthodontic appliances and temporary restorations, however they can not be used as tooth filling materials because they can lead to pulpitis and periodontitis as they may generate heat and acids during curing, and in addition they shrink.

    Failure of dental restorations

    Fillings have a finite lifespan; composites appear to have a higher failure rate than amalgam over five to seven years. How well people keep their teeth clean and avoid cavities is probably a more important factor than the material chosen for the restoration.

    Evaluation and regulation of dental materials

    The Nordic Institute of Dental Materials evaluates dental materials in the Nordic countries. This research and testing institution are accredited to perform several test procedures for dental products. In Europe, dental materials are classified as medical devices according to the Medical Devices Directive. In USA, the U.S. Food and Drug Administration is the regulatory body for dental products.